Crystallization Behavior of Rapid-Compression-Induced Mesomorphic Isotactic Polypropylene during Uniaxial Stretching at Different Temperatures

<div>(a) One-dimensional SAXS curves at specific strains of the initial mesophase and that stretched at 40, 80, and 120°C and (b) variation of the long period as a function of specific strains stretched at 40, 80, and 120°C.</div>

Polymer Crystallization

fig8

Figure 8

Figure 8: Crystallization Behavior of Rapid-Compression-Induced Mesomorphic Isotactic Polypropylene during Uniaxial Stretching at Different Temperatures 

Figure 8 | Crystallization Behavior of Rapid-Compression-Induced Mesomorphic Isotactic Polypropylene during Uniaxial Stretching at Different Temperatures 