Table of Contents
Scholarly Research Exchange
Volume 2009, Article ID 309529, 14 pages
http://dx.doi.org/10.3814/2009/309529
Research Article

An Experimental Study of Thermal Fatigue on ASTM A 213 Grade T-23 Steel Tube

1Department of Production Engineering, National Institute of Technology, Tiruchirappalli-620 015, Tamil Nadu, India
2Welding Research Institute, Bharat Heavy Electricals Limited, Tiruchirappalli-620 014, Tamil Nadu, India

Received 9 January 2009; Revised 12 May 2009; Accepted 20 July 2009

Copyright © 2009 G. R. Jinu et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. M. Hayashi, “Thermal fatigue behavior of thin-walled cylindrical carbon steel specimens in simulated BWR environment,” International Journal of Nuclear Engineering and Design, vol. 184, no. 1, pp. 123–133, 1998. View at Google Scholar
  2. I. Virkkunen, Thermal Fatigue of Austenitic and Duplex Stainless Steels. Acta Polytechnica Scandinavica, Mechanical Engineering Series no. 154, Finnish Academies of Technology, Espoo, Finland, 2001.
  3. T. Yoshimoto, S. Ishihara, T. Goshima, A. J. McEvily, and T. Ishizaki, “Improved method for the determination of the maximum thermal stress induced during a quench test,” Scripta Materialia, vol. 41, no. 5, pp. 553–559, 1999. View at Publisher · View at Google Scholar
  4. A. Tulyakov, “Thermal fatigue in heat power engineering,” Mashinostroyeniye, vol. 197, 1978. View at Google Scholar
  5. A. B. Vainman, R. K. Melekhov, and O. D. Smiyan, Hydrogen Induced Embitterment of High-Pressure Boiler Elements, vol. 272, Naukova Dumka, Kyiv, Russia, 1990.
  6. A. Usman and A. N. Khan, “Failure analysis of heat exchanger tubes,” Engineering Failure Analysis, vol. 15, no. 1-2, pp. 118–128, 2008. View at Publisher · View at Google Scholar
  7. J. P. King and D. B. Riley, “Recent experience in condition assessment of boiler header components and supports,” in Proceedings of the ASME Pressure Vessels and Piping Conference, vol. 333, pp. 135–140, July 1996.
  8. B. J. Smith, C. I. Erskine, R. J. Hartranft, and A. R. Marder, High-Temperature Corrosion-Fatigue (Circumferential) Cracking Life Evaluation Procedure for Low Alloy Cr-Mo) Boiler Tube Steels, Lehigh University, Bethlehem, Pa, USA, 1999.
  9. B. B. Kerezsi, J. W. H. Price, and R. N. Ibrahim, “Using S-N curves to analyse cracking due to repeated thermal shock,” Journal of Materials Processing Technology, vol. 145, no. 1, pp. 118–125, 2004. View at Publisher · View at Google Scholar
  10. Y. H. Choi and S. Y. Choi, “Socket weld integrity in nuclear piping under fatigue loading condition,” Nuclear Engineering and Design, vol. 237, no. 2, pp. 213–218, 2007. View at Publisher · View at Google Scholar
  11. A. Shiblia and F. Starr, “Some aspects of plant and research experience in the use of new high strength martensitic steel T91,” International Journal of Pressure Vessels and Piping, vol. 84, pp. 114–122, 2007. View at Google Scholar
  12. T. B. Brown, “Assessing the effect of thermal transients on the life of boiler plant, Babcock energy limited,” Scotland, 1998.
  13. I. R. Paterson and J. D. Wilson, “Use of damage monitoring systems for component life optimisation in power plant,” International Journal of Pressure Vessels and Piping, vol. 79, no. 8–10, pp. 541–547, 2002. View at Publisher · View at Google Scholar
  14. T. Tokiyoshi, F. Kawashima, T. Igari, and H. Kino, “Crack propagation life prediction of a perforated plate under thermal fatigue,” International Journal of Pressure Vessels and Piping, vol. 78, no. 11-12, pp. 837–845, 2001. View at Google Scholar
  15. B. B. Kerezsi, A. G. Kotousov, and J. W. H. Price, “Experimental apparatus for thermal shock fatigue investigations,” International Journal of Pressure Vessels and Piping, vol. 77, no. 7, pp. 425–434, 2000. View at Publisher · View at Google Scholar
  16. E. E. Underwood and K. Banerji, “Fractal analysis of fracture surfaces,” in ASM Hand Book, vol. 12, Metals Hand Book, 9th edition, 2000. View at Google Scholar