Abstract
A study has been made of the changes in the instantaneous plastic strain ratios along
various directions of α-brass sheet as a function of tensile strain. The α-brass sheet was
fabricated by 88% cold rolling and subsequent annealing at 450℃ for 1.5 h, which lead to
complete recrystallization. The recrystallization texture of the α-brass sheet could be
approximated by {110}