Abstract
Results of texture investigations in sheet and plate of the Al–Li alloy 1441 are presented.
The peculiarities of fracture surface morphology formation during fatigue crack propagation
tests in dependence on texture inhomogeneity are considered. The deviation of the
fatigue crack from the principal direction in center-notched specimens could be related to
occurrence of a {110}