Physicochemical Properties of Epoxy Resin-Based and Bioceramic-Based Root Canal Sealers
Table 2
Chemical compositions of the root canal sealers investigated in the present study.
| Sealer | Components |
| Epoxy resin-based sealer | Radic-Sealer | Base | Catalyst | Poly epoxy resin Zirconium oxide | TEA (triethanolamine) Zirconium oxide Calcium oxide | AD Seal | Base | Catalyst | <20% epoxy resin NS calcium phosphate NS zirconium dioxide NS calcium oxide NS ethylene glycol salicylate | 2.5%–10% N, n-dibenzyl-5-oxanonandiamin-1,9 2.5%–10% amantadine | AH-Plus | Paste A | Paste B | 25%–50% bisphenol A 10%–25% zirconium dioxide NS calcium tungstate NS iron oxide | 2.5%–10% N, n-dibenzyl-5-oxanonandiamin-1,9 2.5%–10% amantadine | Bioceramic-based sealer | EndoSequence BC Sealer | Zirconium oxide, calcium silicates, calcium phosphate monobasic, calcium hydroxide, filler, thickening agents | EndoSeal MTA | Calcium silicates, calcium aluminates, calcium aluminoferrite, calcium sulfates, radiopacifier, thickening agents | MTA Fillapex | Salicylate resin, diluting resin, natural resin, bismuth trioxide, nanoparticulated silica, MTA |
|
|