Research Article
Improvement of Pitting Corrosion Resistance of Type 316L Stainless Steel by Potentiostatic Removal of Surface MnS Inclusions
Figure 3
SEM image and EDS elemental mappings for the same region as in Figure 2 after polarization treatment at 0.5 V for 30 min in 1 M Na2SO4 of pH 3.