Preparation and Anodizing of SiCp/Al Composites with Relatively High Fraction of SiCp
Table 4
The thickness of anodized film after oxidizing for different time.
is the volume fraction of SiC particles.
| | Thickness of anodized film for different oxidizing time (μm) | (%) | 5 min | 10 min | 15 min | 20 min | 25 min | 30 min |
| 68.0 | 12.5 | 14.5 | 15.5 | 17.9 | 18.3 | 19.6 | 67.4 | 12.9 | 15.9 | 17.3 | 20.2 | 22.4 | 24.4 | 63.5 | 13.5 | 16.3 | 19.2 | 21.2 | 23.4 | 26.4 | 61.2 | 16.9 | 18.7 | 20.8 | 23.0 | 24.8 | 27.3 | 60.0 | 17.5 | 19.6 | 22.4 | 24.0 | 26.2 | 28.4 |
|
|