Tests on Pretrained Superelastic NiTi Shape Memory Alloy Rods: Towards Application in Self-Centering Link Beams
Table 3
Forward transformation stress at typical loading cycles.
| Specimens | Forward transformation stress | After incremental cycles | After 5 constant cycles | After 10 constant cycles | After 15 constant cycles | After 20 constant cycles | After 25 constant cycles | σ0 (MPa) | σ0/σ25 | σ5 (MPa) | σ5/σ25 | σ10 (MPa) | σ10/σ25 | σ10 (MPa) | σ10/σ25 | σ10 (MPa) | σ10/σ25 | σ10 (MPa) |
| D14/14-N-N | 674 | 1.06 | 657 | 1.04 | 650 | 1.03 | 644 | 1.02 | 640 | 1.01 | 633 | D14/14-300-30 | 605 | 1.10 | 578 | 1.05 | 568 | 1.04 | 557 | 1.02 | 551 | 1.01 | 548 | D14/14-350-30 | 399 | 1.65 | 313 | 1.29 | 275 | 1.14 | 258 | 1.07 | 244 | 1.01 | 242 | D14/14-400-30 | 360 | 1.95 | 253 | 1.40 | 216 | 1.19 | 202 | 1.12 | 188 | 1.04 | 181 | D14/14-450-30 | 210 | 1.44 | 175 | 1.20 | 163 | 1.12 | 155 | 1.06 | 150 | 1.03 | 146 |
|
|