Experimental and Numerical Analysis of Nonlinear Flexural Behaviour of Lattice-Web Reinforced Foam Core Composite Sandwich Panels
Table 3
Material parameters of the GFRP face sheets.
| Property | LS-DYNA parameter | Experimental value |
| Density | RO | 1.8 g/cm3 | Modulus in longitudinal direction | EA | 20.95 GPa | Modulus in transverse direction | EB | 20.95 GPa | Shear modulus | GAB | 2.5 GPa | Poisson’s ratio | PRBA | 0.15 | Tensile strength in longitudinal direction | XT | 322.9 MPa | Tensile strength in transverse direction | YT | 322.9 MPa | Compressive strength in longitudinal direction | XC | 165.4 MPa | Compressive strength in transverse direction | YC | 165.4 MPa | Shear strength | SC | 55 MPa |
|
|