Research Article
Development of Composite for Thermal Barriers Reinforced by Ceramic Fibers
Table 3
Detailed results of bulk density, flexural strength, and compressive strength.
| | Mixture | | 105°C | | | 600°C | | | 1000°C | | | ρ (kg·m−3) | ftm (MPa) | fcm (MPa) | ρ (kg·m−3) | ftm (MPa) | fcm (MPa) | ρ (kg·m−3) | ftm (MPa) | fcm (MPa) |
| | I-0 | 2300 | 8.2 | 59.8 | 2260 | 5.0 | 55.2 | 2190 | 4.4 | 19.9 | | I-5 | 2375 | 10.8 | 68.3 | 2250 | 4.8 | 47.1 | 2180 | 3.3 | 27.0 | | I-10 | 2340 | 9.0 | 66.8 | 2240 | 3.4 | 47.0 | 2200 | 2.5 | 23.6 | | I-15 | 2320 | 8.6 | 63.5 | 2210 | 3.4 | 42.5 | 2150 | 2.5 | 21.9 | | I-20 | 2310 | 8.0 | 54.5 | 2200 | 4.5 | 41.0 | 2160 | 2.4 | 30.3 | | I-25 | 2290 | 7.3 | 64.2 | 2180 | 4.0 | 36.7 | 2110 | 2.3 | 28.8 |
| | II-0 | 2350 | 8.2 | 78.1 | 2220 | 3.1 | 57.3 | 2215 | 2.0 | 20.9 | | II-5 | 2350 | 9.6 | 73.8 | 2220 | 5.0 | 58.4 | 2195 | 2.3 | 22.3 | | II-10 | 2300 | 9.1 | 63.4 | 2195 | 4.0 | 54.6 | 2170 | 2.8 | 24.2 | | II-15 | 2280 | 10.0 | 58.6 | 2170 | 4.8 | 44.0 | 2090 | 2.7 | 27.9 | | II-20 | 2260 | 8.2 | 56.0 | 2105 | 4.4 | 39.8 | 2070 | 4.0 | 32.8 | | II-25 | 2235 | 6.6 | 55.3 | 2135 | 4.4 | 48.4 | 2120 | 3.9 | 32.8 |
| | III-0 | 2310 | 8.5 | 47.5 | 2240 | 3.7 | 30.6 | 2170 | 2.1 | 27.9 | | III-5 | 2220 | 9.7 | 64.4 | 2100 | 4.2 | 42.4 | 2090 | 2.4 | 22.5 | | III-10 | 2200 | 8.5 | 64.7 | 2120 | 4.2 | 39.7 | 2060 | 2.2 | 20.6 | | III-15 | 2195 | 8.4 | 59.0 | 2090 | 3.7 | 40.2 | 2075 | 2.8 | 25.1 | | III-20 | 2180 | 8.9 | 60.2 | 2040 | 4.8 | 41.3 | 2040 | 3.1 | 25.7 | | III-25 | 2180 | 10.4 | 60.7 | 2050 | 4.7 | 42.1 | 2030 | 3.3 | 28.2 |
|
|