Development of Composite for Thermal Barriers Reinforced by Ceramic Fibers
Table 4
Basic and mechanical properties of hydrothermally cured specimens.
| | | 105°C | 600°C | 1000°C | | ρ (kg·m−3) | fcm (MPa) | ftm (MPa) | Gf (J·m−2) | ρ (kg·m−3) | fcm (MPa) | ftm (MPa) | Gf (J·m−2) | ρ (kg·m−3) | fcm (MPa) | ftm (MPa) | Gf (J·m−2) |
| | II-0HC | 2400 | 91.3 | 20.4 | 294.5 | 2170 | 72.4 | 6.1 | 146.3 | 2130 | 53.0 | 4.6 | 137.4 | | II-5HC | 2390 | 53.7 | 17.5 | 205.4 | 2145 | 46.5 | 4.1 | 178.8 | 2130 | 39.7 | 3.2 | 123.1 | | II-10HC | 2380 | 64.9 | 16.8 | 184.6 | 2135 | 58.5 | 6.0 | 157.9 | 2110 | 42.6 | 3.9 | 143.6 | | II-15HC | 2310 | 59.5 | 14.2 | 131.3 | 2105 | 40.8 | 5.0 | 160.6 | 2085 | 34.6 | 3.3 | 96.0 | | II-20HC | 2305 | 46.8 | 15.9 | 142.3 | 2090 | 37.9 | 5.3 | 139.3 | 2085 | 26.0 | 4.4 | 118.2 | | II-25HC | 2350 | 44.7 | 14.0 | 116.2 | 2155 | 35.6 | 5.7 | 116.6 | 2110 | 27.2 | 4.1 | 125.6 |
|
|