Research Article
Mechanical Properties of Steel Fiber-Reinforced Magnesium Phosphate Cement Mortar
Table 3
Compressive strength and flexural strength of MSFRMM.
| ID | Curing time | 6 h | 12 h | 1 d | 3 d | 7 d | Comp. | Flex. | Comp. | Flex. | Comp. | Flex. | Comp. | Flex. | Comp. | Flex. |
| S/C-0.6 | 21.8 | 7.1 | 33.1 | 8.1 | 47.1 | 10.3 | 54.7 | 11.1 | 60.1 | 13.4 | S/C-0.8 | 32.8 | 8.4 | 42 | 10.6 | 46.1 | 12.5 | 55.4 | 13.2 | 63.8 | 14.3 | S/C-1.0 | 26 | 6.6 | 34.1 | 7.4 | 49.9 | 10.1 | 50.4 | 10.2 | 55.5 | 11.9 | S/C-1.2 | 19.6 | 4.9 | 32.3 | 7.2 | 44.9 | 8.4 | 47.7 | 9.8 | 52.8 | 11.6 | S/C-1.4 | 25.6 | 4.1 | 31.2 | 7.9 | 41.6 | 8.5 | 46.8 | 9.2 | 48.9 | 11.5 | W/C-0.16 | 32.8 | 8.4 | 42 | 10.6 | 46.1 | 12.5 | 55.4 | 13.2 | 63.8 | 14.3 | W/C-0.17 | 31.5 | 7.5 | 39.5 | 10.2 | 48.5 | 12 | 56.5 | 12.2 | 65.8 | 11.8 | W/C-0.18 | 26.1 | 8.3 | 35.1 | 8.3 | 46.4 | 9.9 | 52.8 | 9.1 | 61.2 | 10.6 | W/C-0.19 | 20.9 | 7.1 | 34.2 | 8.1 | 39.4 | 9.4 | 46.1 | 8.7 | 56.2 | 11.1 | W/C-0.20 | 23.8 | 7.6 | 30.2 | 7.7 | 34.7 | 7.9 | 42.8 | 9.5 | 52.1 | 10.7 | MSF-0.0% | 18.5 | 3.0 | 22.9 | 3.8 | 27.6 | 6.3 | 36.2 | 6.1 | 44.4 | 7.4 | MSF-0.4% | 22.3 | 6.5 | 36.6 | 5.5 | 40.2 | 7.9 | 44.7 | 8.8 | 53.6 | 9.9 | MSF-0.8% | 32.8 | 8.4 | 42 | 10.6 | 46.1 | 12.5 | 55.4 | 13.2 | 63.8 | 14.3 | MSF-1.2% | 35.4 | 8.2 | 44.8 | 8.6 | 47.2 | 11.7 | 54.2 | 13.6 | 62.5 | 15 | MSF-1.6% | 36.2 | 9.5 | 47.4 | 11.4 | 50.1 | 15.6 | 58.4 | 16 | 68.2 | 17.4 |
|
|
Note. Comp. and flex. represent compressive strength and flexural strength, respectively.
|