Tensile Mechanical Properties and Failure Modes of a Basalt Fiber/Epoxy Resin Composite Material
Table 3
Calculated values of
and
for the
fiber clustering with different fiber volume fractions.
| | = 0.6% | = 0.9% | = 1.2% | = 1.5% | (mm) | (mm2) | (mm) | (mm2) | (mm) | (mm2) | (mm) | (mm2) |
| 1 | 1.6873 | 0.1297 | 2.2260 | 0.2516 | 1.7707 | 0.1216 | 1.9107 | 0.1247 | 2 | 2.1040 | 0.2116 | 2.0927 | 0.1159 | 1.4033 | 0.0869 | 1.3867 | 0.0752 | 3 | 1.0007 | 0.0566 | 1.5520 | 0.0903 | 1.8380 | 0.1683 | 1.3893 | 0.1380 | 4 | 0.8187 | 0.0493 | 1.6253 | 0.0956 | 1.1933 | 0.0966 | 1.5607 | 0.1260 | 5 | 1.6520 | 0.0930 | 1.7587 | 0.1676 | 1.3293 | 0.0992 | 1.6360 | 0.1342 | 6 | 1.7920 | 0.1739 | 1.7880 | 0.1684 | 1.4427 | 0.1413 | 1.3000 | 0.1041 | 7 | — | — | 1.6073 | 0.1047 | 1.6980 | 0.1489 | 1.5373 | 0.1346 | 8 | — | — | 1.6093 | 0.0887 | 1.4333 | 0.1111 | 1.4927 | 0.1354 | 9 | — | — | 1.3620 | 0.0674 | 1.4267 | 0.1195 | 1.4587 | 0.1337 | 10 | — | — | — | — | 1.1420 | 0.0857 | 1.2833 | 0.0870 | 11 | — | — | — | — | 1.5180 | 0.1199 | 1.4673 | 0.1136 | 12 | — | — | — | — | 1.5467 | 0.1460 | 1.3733 | 0.1151 | 13 | — | — | — | — | 1.5067 | 0.1380 | 1.6620 | 0.1601 | 14 | — | — | — | — | — | — | 1.2527 | 0.0982 | 15 | — | — | — | — | — | — | 1.3993 | 0.1104 | 16 | — | — | — | — | — | — | 1.3820 | 0.1068 | 17 | — | — | — | — | — | — | 1.4807 | 0.1082 | 18 | — | — | — | — | — | — | 1.8280 | 0.1551 | 19 | — | — | — | — | — | — | 1.6640 | 0.1220 |
|
|