Bond Strength between Glass Fiber Fabrics and Low Water-to-Binder Ratio Mortar: Experimental Characterization

<table class="table-group" id="tab1"><tr><td><table class="table"><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr class="thead"><td class="align_left">Component</td><td class="align_center">(%)</td></tr><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr><td class="align_left">CaO</td><td class="align_center">63.1</td></tr><tr><td class="align_left">SiO<sub>2</sub></td><td class="align_center">20.2</td></tr><tr><td class="align_left">Al<sub>2</sub>O<sub>3</sub></td><td class="align_center">2.2</td></tr><tr><td class="align_left">Fe<sub>2</sub></td><td class="align_center">4</td></tr><tr><td class="align_left">MgO</td><td class="align_center">2.0</td></tr><tr><td class="align_left">Na<sub>2</sub>O</td><td class="align_center">0.18</td></tr><tr><td class="align_left">K<sub>2</sub>O</td><td class="align_center">0.31</td></tr><tr><td class="align_left">Loss on ignition</td><td class="align_center">4.5</td></tr><tr><td class="align_left">C<sub>2</sub>S</td><td class="align_center">68</td></tr><tr><td class="align_left">C<sub>3</sub>S</td><td class="align_center">13</td></tr><tr><td class="align_left">C<sub>3</sub>A</td><td class="align_center">1</td></tr><tr><td class="align_left">C<sub>3</sub>AF</td><td class="align_center">13</td></tr><tr class="table-tr"><td colspan="2"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Chemical composition and clinker components of SR cement.</div>

Advances in Civil Engineering

tab1

Table 1

Table 1: Bond Strength between Glass Fiber Fabrics and Low Water-to-Binder Ratio Mortar: Experimental Characterization 