Bond Strength between Glass Fiber Fabrics and Low Water-to-Binder Ratio Mortar: Experimental Characterization

<table class="table-group" id="tab3"><tr><td><table class="table"><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr class="thead"><td class="align_left">Description</td><td class="align_center">Value</td></tr><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr><td class="align_left">Linear density (Tex)</td><td class="align_center">2400</td></tr><tr><td class="align_left">Glass type</td><td class="align_center">E</td></tr><tr><td class="align_left">Filament diameter, nominal (<i>µ</i>m)</td><td class="align_center">17</td></tr><tr><td class="align_left">Glass density (g/cm<sup>3</sup>)</td><td class="align_center">2.54</td></tr><tr><td class="align_left">Fabric weight (g/m<sup>2</sup>)</td><td class="align_center">1000</td></tr><tr class="table-tr"><td colspan="2"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Properties of the glass fabric.</div>

Advances in Civil Engineering

tab3

Table 3

Table 3: Bond Strength between Glass Fiber Fabrics and Low Water-to-Binder Ratio Mortar: Experimental Characterization 