Effect of Sulphate and Chloride Ingress on Selected Cements Mortar Prisms Immersed in Seawater and Leather Industry Effluent
Table 7
Dapp and r2 Values after exposure to WLI for SO42−.
| Cement type | w/c | Dapp (×10−11 m2/s) | r2 | Cs |
| A | 0.5 | 1.0645 | 0.939 | 1600 | 0.6 | 1.3906 | 0.934 | 1500 | 0.65 | 7.8220 | 0.945 | 2100 | 0.7 | 5.4200 | 0.918 | 1800 | B | 0.5 | 1.0600 | 0.939 | 2000 | 0.6 | 1.2200 | 0.936 | 2000 | 0.65 | 1.3900 | 0.934 | 2100 | 0.7 | 9.1800 | 0.942 | 2100 | C | 0.5 | 6.5730 | 0.950 | 1850 | 0.6 | 10.647 | 0.939 | 1600 | 0.65 | 10.647 | 0.939 | 1720 | 0.7 | 12.220 | 0.936 | 2200 |
|
|