Table 5
Sikadur®-30 LP (two-part epoxy impregnation resin).
| Appearance and colours | Part A: white; Part B: black; parts A + B: light grey |
| Density (at 23°C) | ∼1.65 kg/lt (parts A + B) | Mixing ratio | Part A : B = 3 : 1 by weight or volume | Layer thickness | 30 mm max | Open time | 90 minutes (at +25°C) | Viscosity | Pasty, not flowable | Service temperature | –40°C to +45°C (when cured at >+23°C) | Tensile strength | 15 MPa to 18 MPa (when cured for seven days at +23°C) | Shear strength | 17 MPa to 21 MPa [+40°C to +55°C (7 days)] |
|
|