Effect of Fractal-Based Fiber Clustering on Tensile Properties of BFRP
Table 1
Calculated values of
and
with fractal method.
| j | i = 0.6% | i = 0.9% | i = 1.2% | i = 1.5% | (mm) | (mm2) | (mm) | (mm2) | (mm) | (mm2) | (mm) | (mm2) |
| 1 | 1.7432 | 0.1027 | 2.3216 | 0.1995 | 1.8216 | 0.0817 | 2.0516 | 0.0995 | 2 | 2.1893 | 0.1763 | 2.1325 | 0.0838 | 1.5367 | 0.0841 | 1.4216 | 0.1071 | 3 | 1.2563 | 0.0434 | 1.6824 | 0.0788 | 1.9421 | 0.1146 | 1.4452 | 0.1132 | 4 | 0.9864 | 0.0391 | 1.9387 | 0.0763 | 1.2673 | 0.1171 | 1.6457 | 0.0906 | 5 | 1.9322 | 0.078 | 1.8632 | 0.1363 | 1.4683 | 0.0934 | 1.7683 | 0.1074 | 6 | 1.8861 | 0.0703 | 1.8914 | 0.139 | 1.5214 | 0.0665 | 1.4519 | 0.106 | 7 | — | — | 1.7325 | 0.0815 | 1.7658 | 0.0961 | 1.7218 | 0.1064 | 8 | — | — | 1.8106 | 0.0652 | 1.5416 | 0.0888 | 1.6457 | 0.0698 | 9 | — | — | 1.4563 | 0.0524 | 1.5317 | 0.0697 | 1.7549 | 0.0954 | 10 | — | — | — | — | 1.2549 | 0.1022 | 1.4318 | 0.0895 | 11 | — | — | — | — | 1.2463 | 0.1162 | 1.5673 | 0.1316 | 12 | — | — | — | — | 1.6715 | 0.116 | 1.4983 | 0.0762 | 13 | — | — | — | — | 1.6124 | 0.1275 | 1.8473 | 0.0846 | 14 | — | — | — | — | — | — | 1.3981 | 0.0893 | 15 | — | — | — | — | — | — | 1.5428 | 0.0907 | 16 | — | — | — | — | — | — | 1.4672 | 0.0887 | 17 | — | — | — | — | — | — | 1.6427 | 0.0574 | 18 | — | — | — | — | — | — | 1.946 | 0.0801 | 19 | — | — | — | — | — | — | 1.917 | 0.0944 |
|
|