Experimental Research on the Influence of Temperature on the Static Properties of Skarn
Table 3
Brazilian disc splitting experiment test data (natural cooling).
| Specimen number | Temperature (°C) | Diameter (mm) | Thickness (mm) | Quality (g) | Failure load (kN) | Tensile strength (MPa) | Average value (MPa) |
| LKL-1 | 25 | 50 | 40.45 | 275 | 44.13 | 11.12 | | LKL-2 | 25 | 50 | 40.00 | 268 | 66.58 | 16.96 | 14.27 | LKL-3 | 25 | 50 | 40.20 | 256 | 58.14 | 14.74 | | LKL-4 | 200 | 50 | 40.70 | 280 | 35.56 | 8.90 | | LKL-5 | 200 | 50 | 40.60 | 266 | 34.56 | 8.68 | 8.88 | LKL-6 | 200 | 50 | 39.9 | 245 | 35.44 | 9.05 | | LKL-7 | 400 | 50 | 41.4 | 282 | 28.86 | 7.10 | | LKL-8 | 400 | 50 | 40 | 275 | 28.8 | 7.34 | 7.05 | LKL-9 | 400 | 50 | 40 | 265 | 26.38 | 6.72 | | LKL-10 | 600 | 50 | 40.8 | 255 | 20.26 | 5.06 | | LKL-11 | 600 | 50 | 41.4 | 271 | 22.40 | 5.51 | 5.37 | LKL-12 | 600 | 50 | 40.1 | 267 | 21.76 | 5.53 | | LKL-13 | 800 | 50 | 41 | 267 | 14.61 | 3.63 | | LKL-14 | 800 | 50 | 39.7 | 246 | 13.54 | 3.48 | 3.64 | LKL-15 | 800 | 50 | 40.4 | 282 | 15.06 | 3.80 | |
|
|
Note. LKL represents the test piece used for Brazilian disc splitting experiment after air cooling.
|