Flexural Performance of Emulsified-Asphalt-Modified ECC for Expansion Joint Use
Table 4
Flexural mechanical properties of EA-ECCs under four-point bending test.
| Mix | First cracking strength | Ultimate flexural stress | Deflection capacity |
| E0 | 6.17 ± 0.54 MPa | 11.87 ± 0.34 MPa | 9.01 ± 0.77 mm | E1 | 5.67 ± 0.78 MPa | 9.57 ± 0.81 MPa | 18.32 ± 3.34 mm | E2 | 6.53 ± 0.31 MPa | 9.01 ± 0.05 MPa | 17.15 ± 1.05 mm | E3 | 5.43 ± 0.42 MPa | 9.15 ± 0.19 MPa | 26.60 ± 1.95 mm | E4 | 4.06 ± 1.02 MPa | 7.13 ± 0.71 MPa | 33.32 ± 2.65 mm |
|
|