Research Article
Establishment of a Shear Strength Prediction Model for Asphalt Mixtures with Raw Materials Properties and Design Parameters
Table 4
Shear strength of 101 sets of asphalt mixtures.
| Grading | Gyratory number | Asphalt type | Asphalt-aggregate ratio (%) | Shear strength (MPa) |
| Sup13-1 | 50 | 70# | 4.3 | 0.423 | Sup13-1 | 50 | 70# | 4.7 | 0.463 | Sup13-1 | 50 | 70# | 5.1 | 0.499 | Sup13-1 | 50 | 70# | 5.5 | 0.777 | Sup13-1 | 75 | 70# | 4.1 | 0.514 | Sup13-1 | 75 | 70# | 4.4 | 0.537 | Sup13-1 | 75 | 70# | 4.7 | 0.563 | Sup13-1 | 75 | 70# | 5.0 | 0.801 | Sup13-1 | 100 | 70# | 4.1 | 0.541 | Sup13-1 | 100 | 70# | 4.4 | 0.586 | Sup13-1 | 100 | 70# | 4.7 | 0.668 | Sup13-1 | 100 | 70# | 5.0 | 0.916 | Sup13-1 | 125 | 70# | 4.1 | 0.609 | Sup13-1 | 125 | 70# | 4.4 | 0.695 | Sup13-1 | 125 | 70# | 4.7 | 0.813 | Sup13-1 | 125 | 70# | 5.0 | 1.110 | Sup13-1 | 50 | Polymer | 4.7 | 0.895 | Sup13-1 | 75 | Polymer | 4.7 | 1.102 | Sup13-1 | 100 | Polymer | 4.7 | 1.205 | Sup13-1 | 125 | Polymer | 4.7 | 1.273 | Sup13-2 | 50 | 70# | 4.3 | 0.495 | Sup13-2 | 50 | 70# | 4.7 | 0.527 | Sup13-2 | 50 | 70# | 5.1 | 0.570 | Sup13-2 | 50 | 70# | 5.5 | 0.789 | Sup13-2 | 75 | 70# | 4.3 | 0.600 | Sup13-2 | 75 | 70# | 4.7 | 0.668 | Sup13-2 | 75 | 70# | 5.1 | 0.853 | Sup13-2 | 75 | 70# | 5.5 | 0.978 | Sup13-2 | 100 | 70# | 4.1 | 0.564 | Sup13-2 | 100 | 70# | 4.4 | 0.692 | Sup13-2 | 100 | 70# | 4.7 | 0.851 | Sup13-2 | 100 | 70# | 5.0 | 0.956 | Sup13-2 | 125 | 70# | 4.1 | 0.754 | Sup13-2 | 125 | 70# | 4.4 | 0.850 | Sup13-2 | 125 | 70# | 4.7 | 1.014 | Sup13-2 | 125 | 70# | 5.0 | 1.141 | Sup13-2 | 50 | Polymer | 4.7 | 1.032 | Sup13-2 | 75 | Polymer | 4.7 | 1.170 | Sup13-2 | 100 | Polymer | 4.7 | 1.260 | Sup13-2 | 125 | Polymer | 4.7 | 1.350 | Sup13-5 | 75 | Polymer | 4.3 | 1.130 | Sup13-5 | 75 | Polymer | 4.7 | 1.160 | Sup13-5 | 100 | Polymer | 4.7 | 1.347 | Sup13-5 | 125 | Polymer | 4.7 | 1.487 | Sup13-5 | 75 | Polymer | 5.1 | 1.310 | Sup13-5 | 75 | Polymer | 5.5 | 1.290 | Sup13-5 | 75 | 70# | 4.7 | 0.640 | Sup13-6 | 100 | Polymer | 4.3 | 1.177 | Sup13-6 | 75 | Polymer | 4.7 | 0.950 | Sup13-6 | 100 | Polymer | 4.7 | 1.247 | Sup13-6 | 125 | Polymer | 4.7 | 1.370 | Sup13-3 | 50 | 70# | 4.7 | 0.427 | Sup13-3 | 50 | 70# | 5.1 | 0.434 | Sup13-3 | 50 | 70# | 5.5 | 0.451 | Sup13-3 | 50 | 70# | 5.9 | 0.572 | Sup13-3 | 75 | 70# | 4.3 | 0.446 | Sup13-3 | 75 | 70# | 4.7 | 0.496 | Sup13-3 | 75 | 70# | 5.1 | 0.597 | Sup13-3 | 75 | 70# | 5.5 | 0.720 | Sup13-3 | 100 | 70# | 4.3 | 0.738 | Sup13-3 | 100 | 70# | 4.7 | 0.793 | Sup13-3 | 100 | 70# | 5.1 | 0.951 | Sup13-3 | 100 | 70# | 5.5 | 1.047 | Sup13-3 | 125 | 70# | 4.1 | 0.592 | Sup13-3 | 125 | 70# | 4.4 | 0.700 | Sup13-3 | 125 | 70# | 4.7 | 0.921 | Sup13-3 | 125 | 70# | 5.0 | 1.256 | Sup13-3 | 50 | Polymer | 4.7 | 0.902 | Sup13-3 | 75 | Polymer | 4.7 | 1.088 | Sup13-3 | 100 | Polymer | 4.7 | 1.238 | Sup13-3 | 125 | Polymer | 4.7 | 1.302 | Sup13-4 | 50 | 70# | 4.7 | 0.296 | Sup13-4 | 50 | 70# | 5.1 | 0.482 | Sup13-4 | 50 | 70# | 5.5 | 0.578 | Sup13-4 | 50 | 70# | 5.9 | 0.626 | Sup13-4 | 75 | 70# | 4.7 | 0.448 | Sup13-4 | 75 | 70# | 5.1 | 0.739 | Sup13-4 | 75 | 70# | 5.5 | 0.855 | Sup13-4 | 75 | 70# | 5.9 | 0.962 | Sup13-4 | 100 | 70# | 4.3 | 0.602 | Sup13-4 | 100 | 70# | 4.7 | 0.655 | Sup13-4 | 100 | 70# | 5.1 | 0.804 | Sup13-4 | 100 | 70# | 5.5 | 1.083 | Sup13-4 | 125 | 70# | 4.3 | 0.753 | Sup13-4 | 125 | 70# | 4.7 | 0.882 | Sup13-4 | 125 | 70# | 5.1 | 1.006 | Sup13-4 | 125 | 70# | 5.5 | 1.248 | Sup13-4 | 50 | Polymer | 4.7 | 0.856 | Sup13-4 | 75 | Polymer | 4.7 | 0.992 | Sup13-4 | 100 | Polymer | 4.7 | 1.221 | Sup13-4 | 125 | Polymer | 4.7 | 1.369 | Sup13-6 | 100 | Polymer | 5.1 | 1.380 | Sup13-6 | 100 | Polymer | 5.5 | 1.250 | Sup13-6 | 100 | 70# | 4.7 | 0.710 | Sup13-7 | 125 | Polymer | 4.3 | 1.253 | Sup13-7 | 75 | Polymer | 4.7 | 0.720 | Sup13-7 | 100 | Polymer | 4.7 | 1.030 | Sup13-7 | 125 | Polymer | 4.7 | 1.363 | Sup13-7 | 125 | Polymer | 5.1 | 1.500 | Sup13-7 | 125 | Polymer | 5.5 | 1.313 | Sup13-7 | 125 | 70# | 4.7 | 0.770 |
|
|