Nanoprocessing of Industrial Rejects for Controlling Operational Energy of Buildings
Table 4
XRF analysis of before and after milled samples.
| Sample ID/composition | GBFS -WM | GBFS-10 | GBFS-30 | GBFS-90 | OPC cement | IS 3812: 2013 |
| Na2O | 0.38 | 0.2 | 0.2 | 0.2 | — | 1.5 max | MgO | 7.61 | 8.0 | 8.45 | 8.5 | 3.4 | 5 max | Al2O3 | 12.24 | 12.76 | 13.69 | 14.67 | 5.5 | — | SiO2 | 31.76 | 31.63 | 31.71 | 32.11 | 25.1 | 35 min | P2O5 | 0.01 | 0.01 | 0.01 | 0.01 | — | — | SO3 | 1.75 | 1.76 | 1.73 | 1.69 | 2.7 | 3 max | K2O | 0.6 | 0.61 | 0.65 | 0.69 | 0.5 | — | CaO | 43.36 | 42.31 | 41.85 | 40.75 | 55 | — | TiO2 | 0.52 | 0.53 | 0.53 | 0.51 | — | — | MnO2 | 0.29 | 0.03 | 0.3 | 0.32 | — | — | Fe2O3 | 0.46 | 0.61 | 0.41 | 0.40 | 5.9 | — | LOI | 0.68 | 1.26 | 0.19 | 0.15 | 0.9 | 5 Max | Al + Si + Fe | 44.46 | 45 | 45.81 | 46.18 | 36.5 | 70 min |
|
|