Experimental Study on the Effect of Large Temperature Difference on Compressive Strength and Pore Structure of Semirigid Base
Table 4
Uniaxial compression experimental results of semirigid base material under the temperature range of −20°C∼20°C.
| Number of cycles | Parallel strength test value (Mpa) | Intensity representative value (MPa) | Standard deviation | Coefficient of variation (%) |
| 0 | 10.61 | 12.82 | 14.06 | 12.50 | 1.75 | 13.95 | 3 | 11.00 | 11.50 | 13.49 | 12.00 | 1.32 | 10.98 | 6 | 9.61 | 12.61 | 9.79 | 10.67 | 1.68 | 15.77 | 9 | 8.61 | 8.72 | 8.89 | 8.74 | 0.14 | 1.61 | 12 | 7.47 | 8.21 | 6.78 | 7.49 | 0.72 | 9.55 | 15 | 6.59 | 5.38 | 6.53 | 6.16 | 0.67 | 10.93 |
|
|