Performance of Ladle Furnace Slag in Mortar under Standard and Accelerated Curing
Table 2
Chemical composition of CEM-I and raw LFS used in this study.
| Oxides | CEM-I (this study) | Raw LFS (this study) | Raw LFS [54] | Raw LFS [8] |
| CaO (%) | 60.4 | 47.4 | 48.4 | 30∼60 | SiO2 (%) | 29.4 | 29.4 | 15 | 2∼35 | Al2O3 (%) | 2.6 | 2.6 | 14.3 | 4.1∼35.9 | Fe2O3 (%) | 2.8 | 0.7 | 1.5 | — | FeO (%) | — | — | — | 0∼15 | MgO (%) | 2 | 2.3 | 15.3 | 1∼12.6 | Na2O (%) | 1.5 | 1.6 | 0.4 | 0.06∼0.07 | K2O (%) | 0.7 | 0.1 | 0.4 | 0.01∼0.02 | TiO2 (%) | 0.6 | 0.9 | 0.2 | 0.2∼0.9 | MnO (%) | 0.04 | 1.6 | - | 0∼5 |
|
|