Preparation and Characterization of Manganese Ferrite Aluminates
Table 4
Room
temperature Mössbauer’s effect parameters for MnAl x Fe2.0−xO4 system as a function of x.
| Composition () | site | Isomer | Quadrupole splitting | | Area (%) | Fe3+(B)/Fe3+(A) | () mm/s | (Δ) mm/s | (±2.0 T) |
| 0.0 | B |
0.18 | 0.00 | 47.71 | 77.74 | 3.49 | | A | 0.11 | 0.00 | 43.48 | 22.26 | | 0.2 | B |
0.17 | 0.00 | 47.16 | 75.15 | 3.02 | | A | 0.11 | 0.00 | 42.71 | 24.85 | | 0.4 | B | 0.16 | 0.00 | 46.46 | 72.01 | 2.57 | | A | 0.10 | 0.00 | 42.41 | 27.99 | | 0.6 | B | 0.13 | 0.00 | 45.34 | 68.92 | 2.20 | | A | 0.10 | 0.00 | 40.58 | 31.08 | | 0.8 | B | 0.12 | 0.00 | 42.82 | 62.88 | 1.69 | | A | 0.10 | 0.00 | 36.94 | 37.12 | | 1.0 | B | 0.11 | 0.00 | 41.80 | 55.90 | 1.26 | | A | 0.10 | 0.00 | 36.54 | 44.10 | |
|
|
shift given relative to -Fe.
|