Compositional Dependence of Structural Properties of Prepared Alloys and Films
Table 2
X-ray diffraction data for
alloys as bulks.
| Alloy | | ()stand | (Å) | 2θ | (Å) | (Å) | μm x10−1 | () |
| Pb0.50S0.50 | 111 | 84 | 3.429 | 26.15 | 3.404 | 5.900 | 0.407 | 100.00 | 200 | 100 | 2.696 | 30.20 | 2.958 | 5.920 | 0.411 | 100.00 | 220 | 57 | 2.099 | 43.20 | 2.092 | 5.920 | 0.427 | 75.00 | 311 | 35 | 1.790 | 51.175 | 1.783 | 5.914 | 0.440 | 55.00 | 222 | 16 | 1.714 | 53.575 | 1.709 | 5.92 | 0.445 | 35.00 |
| Pb0.51S0.49 | 111 | 84 | 3.429 | 26.20 | 3.400 | 5.900 | 0.329 | 55.00 | 200 | 100 | 2.969 | 30.20 | 2.960 | 5.920 | 0.326 | 100.00 | 220 | 57 | 2.099 | 42.80 | 2.108 | 5.960 | 0.341 | 48.40 | 311 | 35 | 1.790 | 50.6 | 1.8 | 5.96 | 0.263 | 27.60 | 222 | 16 | 1.714 | 52.9 | 1.72 | 5.95 | 0.266 | 24.00 |
| Pb0.52S0.48 | 111 | 84 | 3.429 | 25.70 | 3.451 | 5.970 | 0.244 | 78.00 | 200 | 100 | 2.969 | 30.00 | 2.973 | 5.946 | 0.282 | 100.00 | 220 | 57 | 2.099 | 42.80 | 2.106 | 5.950 | 0.256 | 22.00 | 311 | 35 | 1.790 | 50.8 | 1.792 | 5.94 | 0.211 | 15.00 | 222 | 16 | 1.714 | 53.2 | 1.717 | 5.947 | 0.266 | 16.00 |
| Pb0.54S0.46 | 111 | 84 | 3.429 | 25.60 | 3.470 | 6.000 | 0.325 | 35.00 | 200 | 100 | 2.969 | 30.20 | 2.960 | 5.920 | 0.246 | 100.00 | 220 | 57 | 2.099 | 42.10 | 2.140 | 6.000 | 0.340 | 11.00 |
| Pb0.55S0.45 | 111 | 84 | 3.429 | 25.60 | 3.470 | 6.010 | 0.326 | 15.28 | 200 | 100 | 2.969 | 30.00 | 2.973 | 5.946 | 0.246 | 100.00 |
|
|