Polar Liquid Crystal Elastomers Cross Linked Far from Thermodynamic Phase Transitions: Dislocation Loops in Smectic Clusters
Figure 8
Azimuthal ( in Figure 7) intensity profiles of the small angle peaks at several temperatures for CN50, CN70, and CN100. The intensities are normalized by the background levels due to the polymer backbones. In CN70 and CN100, the peak height (intensity) as well as the peak area are maximum near C.