Advances in Condensed Matter Physics / 2013 / Article / Tab 1

Research Article

Electrical Transport Properties of (Bi1.6Pb0.4Sr2Ca2Cu3O10)/Ag Tapes with Different Nanosized MgO

Table 1

(at 0 T) of  wt.%,  wt.% of 20 nm MgO, and  wt.% of 40 nm MgO added pellets and tapes sintered for 50 h and 100 h at 30 and 77 K.

(wt.%) (30 K) Pellet
(A/cm2)
(77 K) Pellet
(A/cm2)
(30 K) Tape (50 h)
(A/cm2)
(77 K) Tape (50 h)
(A/cm2)
(30 K) Tape (100 h)
(A/cm2)
(77 K) Tape (100 h)
(A/cm2)

0.000.650.318104949108201262
0.10 (20 nm)4.131.73151101532183803676
0.01 (40 nm)2.601.1713120131214060 1875

We are committed to sharing findings related to COVID-19 as quickly as possible. We will be providing unlimited waivers of publication charges for accepted research articles as well as case reports and case series related to COVID-19. Review articles are excluded from this waiver policy. Sign up here as a reviewer to help fast-track new submissions.