Effect of <i>In Situ</i> Thermal Annealing on Structural, Optical, and Electrical Properties of CdS/CdTe Thin Film Solar Cells Fabricated by Pulsed Laser Deposition

<div>Raman spectra of five samples treated with different iTAP durations at 450°C. Peaks corresponding to the CdTe TO, LO, and 2TO modes as well as a signature peak of <svg height="12.0575pt" id="M9" style="vertical-align:-3.2911pt" version="1.1" viewbox="-0.0498162 -8.7664 27.8605 12.0575" width="27.8605pt" xmlns="http://www.w3.org/2000/svg" xmlns:xlink="http://www.w3.org/1999/xlink"><g transform="matrix(.013,0,0,-0.013,0,0)"><path d="M592 498C586 556 582 629 581 675H560C545 656 537 650 510 650H115C87 650 74 652 60 675H40C38 620 33 555 28 495H57C69 539 77 568 89 585C102 607 122 616 205 616H267V123C267 44 259 34 168 28V0H454V28C360 34 352 44 352 123V616H422C498 616 514 608 531 584C542 568 552 543 562 495L592 498Z" id="g121-82"></path><glyph.data ascent="989" descent="-360" horiz-adv-x="617" vert-adv-y="617"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,6.742,0)"><path d="M380 106C343 72 306 56 265 56C195 56 116 112 115 248C235 252 361 262 377 265C396 269 400 277 400 297C400 374 333 449 250 449H249C198 449 144 421 103 376S37 269 37 201C37 88 109 -12 232 -12C263 -12 332 6 395 84L380 106ZM225 412C281 412 315 364 314 312C314 297 308 292 290 292C232 290 176 289 120 289C135 370 180 412 225 412Z" id="g121-99"></path><glyph.data ascent="989" descent="-360" horiz-adv-x="425" vert-adv-y="425"></glyph.data></g><g transform="matrix(.013,0,0,-0.013,12.267,0)"><path d="M381 665C170 665 44 498 44 318C44 125 188 -15 369 -15C552 -15 703 117 703 333C703 534 550 665 381 665ZM359 629C491 629 601 517 601 306C601 114 502 21 390 21C249 21 146 158 146 346S248 629 359 629Z" id="g121-77"></path><glyph.data ascent="989" descent="-360" horiz-adv-x="747" vert-adv-y="747"></glyph.data></g><g transform="matrix(.0091,0,0,-0.0091,21.978,3.132)"><path d="M545 403C545 425 527 451 498 451C448 451 400 404 312 286L290 341C262 412 246 451 219 451C182 451 138 404 92 345L112 323C152 368 169 378 181 378C192 378 201 359 216 321L257 214C184 115 142 69 113 69C102 69 93 73 88 79S78 89 68 89C47 89 24 61 24 40C24 8 49 -12 75 -12C125 -12 175 31 271 175L312 64C330 15 357 -12 382 -12C421 -12 475 35 515 98L496 121C466 88 439 62 420 62C402 62 384 92 363 147L325 247C349 280 374 309 397 333C422 361 446 381 462 381C471 381 481 374 488 366C493 360 499 357 505 357C521 357 545 380 545 403Z" id="g50-121"></path><glyph.data ascent="3443" descent="-2856" horiz-adv-x="569" vert-adv-y="569"></glyph.data></g></svg> can be observed at Raman shifts of 141, 169, 292, and 730 cm<sup>−1</sup>, respectively.</div>

Advances in Condensed Matter Physics

fig4

Figure 4

Figure 4: Effect of <i>In Situ</i> Thermal Annealing on Structural, Optical, and Electrical Properties of CdS/CdTe Thin Film Solar Cells Fabricated by Pulsed Laser Deposition 

Figure 4 | Effect of In Situ Thermal Annealing on Structural, Optical, and Electrical Properties of CdS/CdTe Thin Film Solar Cells Fabricated by Pulsed Laser Deposition 