Research Article
Physical Structure Induced Hydrophobicity Analyzed from Electrospinning and Coating Polyvinyl Butyral Films
Table 1
The SWCA of the prepared PVB films by different methods.
| Methods | SWCA (°) | SWCA (°) | SWCA (°) | ASWCA (°) |
| Concentrations/parameters | 8 wt% | 10 wt% | 12 wt% | | Spin-coating | 250 r/s | 77.767 | 78.800 | 78.900 | 78.593 | 300 r/s | 74.300 | 82.600 | 79.933 | 350 r/s | 76.033 | 82.733 | 76.267 | Bar-coating | 6 μm | 86.438 | 83.297 | 84.303 | 83.067 | 8 μm | 81.255 | 82.626 | 81.437 | 10 μm | 81.093 | 81.360 | 85.796 | Positive electrospinning | 15 cm | 135.833 | 130.833 | 131.933 | 132.404 | 20 cm | 132.167 | 133.600 | 129.700 | 25 cm | 131.667 | 135.400 | 130.500 | Negative electrospinning | 15 cm | 131.033 | 135.733 | 130.867 | 131.615 | 20 cm | 128.633 | 135.100 | 133.367 | 25 cm | 128.300 | 133.233 | 128.267 |
|
|