Study of the Effect of Quenching on Microstructural and Magnetic Properties of Cu-Doped Mg-Ferrite
Table 3
Mossbauer parameters for furnace-cooled and quenched Mg1-xCuxFe2O4 samples after sintering at 1200°C.
| Copper content | Site occupancy | Isomer shift, δ (mm/s) | Quadrupole splitting, (mm/s) | Hyperfine field, Hhf (kG) | Relative area, A (%) | Furnace-cooled | Quenched | Furnace-cooled | Quenched | Furnace-cooled | Quenched | Furnace-cooled | Quenched |
| x = 0.0 | B | 0.330 | 0.314 | 0.232 | 0.080 | 493.583 | 483.181 | 61.9 | 61.8 | B | 0.286 | 0.265 | 0.000 | 0.000 | 473.591 | 460.300 | A | 0.330 | 0.251 | 0.431 | 0.499 | 429.129 | 389.011 | 38.1 | 38.2 | A | 0.262 | 0.331 | 0.000 | 0.828 | 456.518 | 430.809 |
| x = 0.1 | B | 0.383 | 0.316 | 0.362 | 0.000 | 479.924 | 479.369 | 61.1 | 62.4 | B | 0.428 | 0.278 | 0.152 | 0.000 | 475.169 | 460.032 | A | 0.459 | 0.375 | 0.444 | 0.000 | 450.737 | 406.684 | 38.9 | 37.6 | A | 0.273 | 0.290 | 0.433 | 0.000 | 363.255 | 441.204 |
| x = 0.2 | B | 0.452 | 0.314 | 0.499 | 0.191 | 468.198 | 488.309 | 61.8 | 62.8 | B | 0.260 | 0.291 | 0.293 | 0.000 | 471.252 | 466.933 | A | 0.349 | 0.337 | 0.037 | 0.000 | 438.897 | 412.492 | 38.2 | 37.2 | A | 0.434 | 0.277 | 0.000 | 0.020 | 412.217 | 447.696 |
| x = 0.3 | B | 0.323 | 0.308 | 0.009 | 0.202 | 490.436 | 483.249 | 61.8 | 63.1 | B | 0.272 | 0.274 | 0.000 | 0.000 | 468.369 | 460.480 | A | 0.324 | 0.321 | 0.216 | 0.269 | 415.907 | 387.688 | 38.2 | 36.9 | A | 0.282 | 0.279 | 0.000 | 0.020 | 450.879 | 438.040 |
| x = 0.4 | B | 0.339 | 0.344 | 0.080 | 0.090 | 495.884 | 487.695 | 62.4 | 63.8 | B | 0.273 | 0.294 | 0.000 | 0.000 | 470.346 | 464.775 | A | 0.276 | 0.265 | 0.000 | 0.462 | 400.490 | 445.160 | 37.6 | 36.2 | A | 0.291 | 0.393 | 0.388 | 0.008 | 450.624 | 413.646 |
| x = 0.5 | B | 0.369 | 0.343 | 0.138 | 0.050 | 496.815 | 485.470 | 62.9 | 63.3 | B | 0.278 | 0.281 | 0.000 | 0.070 | 473.511 | 462.075 | A | 0.323 | 0.378 | 0.757 | 0.000 | 414.853 | 401.219 | 37.1 | 36.7 | A | 0.276 | 0.303 | 0.000 | 0.738 | 454.298 | 440.170 |
|
|