Designing Novel Interfaces via Surface Functionalization of Short-Chain-Length Polyhydroxyalkanoates
Table 1
Thermal and mechanical properties of various composition of P(3HB-co-3HV) copolymer [
18].
| | Melting temperature | Glass transition temperature | Young’s modulus | Tensile strength | (°C) | (°C) | (GPa) | (MPa) |
| Polypropylene | 176 | -10 | 1.7 | 38 | Poly(ethylene terephthalate) | 267 | 69 | 2.9 | 70 | Nylon-6,6 | 265 | 50 | 2.8 | 83 | Low-density polyethylene | 130 | -30 | 0.2 | 10 | P(3HB) | 179 | 10 | 3.5 | 40 | P(3HB-co-3 mol% 3HV) | 170 | 8 | 2.9 | 38 | P(3HB-co-9 mol% 3HV) | 162 | 6 | 1.9 | 37 | P(3HB-co-14 mol% 3HV) | 150 | 4 | 1.5 | 35 | P(3HB-co-20 mol% 3HV) | 145 | -1 | 1.2 | 32 | P(3HB-co-25 mol% 3HV) | 137 | -6 | 0.7 | 30 |
|
|