Effect on Mechanical and Thermal Properties of Random Copolymer Polypropylene/Microcrystalline Cellulose Composites Using T-ZnOw as an Additive
Table 5
Nonisothermal crystallization parameters of pure rPP and rPP based composites.
| Samples | Cooling rate | | | | | | t1/2 | (°C·min−1) | (J·g−1) | (°C) | (°C) | (s−1) | (min) |
| rPP | 10 | 58.4 | 127.4 | 123.6 | 3.4 | 0.8 | 1.2 | 20 | 60.5 | 124.3 | 120.2 | 3.2 | 6.8 | 0.6 | 30 | 59.2 | 122.2 | 118.0 | 3.5 | 28.4 | 0.4 | 40 | 56.6 | 120.2 | 115.3 | 3.6 | 91.2 | 0.3 | 50 | 61.1 | 119.3 | 113.9 | 3.1 | 86.2 | 0.3 |
| MCC/rPP | 10 | 60.2 | 122.2 | 118.2 | 3.9 | 1.5 | 0.7 | 20 | 62.3 | 118.5 | 113.4 | 4.2 | 9.7 | 0.5 | 30 | 60.0 | 116.3 | 111.0 | 4.1 | 38.7 | 0.4 | 40 | 57.0 | 113.8 | 108.3 | 3.6 | 64.9 | 0.3 | 50 | 62.8 | 112.4 | 106.1 | 3.3 | 54.6 | 0.3 |
| MCC/PP-g-MA/rPP | 10 | 64.6 | 126.4 | 120.2 | 3.5 | 0.7 | 0.9 | 20 | 72.6 | 120.9 | 114.7 | 3.9 | 11.2 | 0.4 | 30 | 72.0 | 118.3 | 111.7 | 3.3 | 18.2 | 0.3 | 40 | 72.3 | 116.8 | 109.7 | 3.8 | 113.9 | 0.3 | 50 | 74.9 | 116.2 | 107.9 | 3.6 | 112.9 | 0.2 |
| T-ZnOw/MCC/PP-g-MA/rPP | 10 | 57.4 | 128.3 | 123.4 | 3.5 | 1.5 | 0.8 | 20 | 72.3 | 121.0 | 115.1 | 3.6 | 9.2 | 0.6 | 30 | 69.4 | 119.3 | 113.9 | 4.1 | 42.7 | 0.3 | 40 | 67.4 | 119.0 | 113.3 | 3.9 | 96.0 | 0.3 | 50 | 70.0 | 118.4 | 112.9 | 4.0 | 129.8 | 0.2 |
|
|