Carbon Nanotube Layer for Reduction of Fiber Print-Through in Carbon Fiber Composites
Table 2
Composites prepared and their characteristics.
| Sample designation | Top layer added? | CNT type and loading | # of CFRP layers | CNT dispersion method |
| IM7 | No | - - - | - - - | - - - |
| IM7/LY556 | Resin | - - - | 7 | - - - |
| IM7/1T | Resin + CNTs | 1 wt.% thermally oxidized | 7 | Mechanical Stirrer |
| IM7/1A | Resin + CNTs | 1 wt.% acid oxidized | 7 | Mechanical Stirrer |
| IM7/1TD | Resin + CNTs | 1 wt.% thermally oxidized with dispersing agent | 7 | Mechanical Stirrer |
| IM7/1AP | Resin + CNTs | 1 wt.% as produced | 7 | Mechanical Stirrer |
| IM7/1AP(4)-3R | Resin + CNTs | 1 wt.% as produced | 4 | Mechanical Stirrer +Three-roll miller machine |
| IM7/1AP-3R | Resin + CNTs | 1 wt.% as produced | 7 | Mechanical Stirrer + Three-roll miller machine |
| IM7/2AP-3R | Resin + CNTs | 2 wt.% as produced | 7 | Mechanical Stirrer +Three-roll miller machine |
|
|