Effect of Zinc Borate on Flammability of PET Woven Fabrics
Table 1
The flame retardant treatment conditions of PET fabrics.
| Finishing agent and application conditions | Quantity (g/l) | Z50 | Z100 | Z200 | PSY | PSY-Z20 | PEK | PEK- Z25 | PEK-Z50 |
| Agent A (PSY) | 0 | 0 | 0 | 80 | 60 | 0 | 0 | 0 | Agent B (PEK) | 0 | 0 | 0 | 0 | 0 | 100 | 75 | 50 | ZnB dispersion | 50 | 100 | 200 | 0 | 20 | 0 | 25 | 50 | Pick-up (%) | 92.35 | 91.25 | 90.75 | 87.74 | 97.20 | 90.87 | 90.60 | 89.30 | pH | 5.5 | 5.5 | 5.5 | 5.0 | 5.0 | 6.0 | 6.0 | 6.0 | Drying | 120°C | 120°C | 120°C | 120°C | 120°C | 120°C | 120°C | 120°C | 2 min. | 2 min. | 2 min. | 1.5 min. | 1.5 min. | 1.5 min. | 1.5 min. | 1.5 min. | Curing | 160°C | 160°C | 160°C | 190°C | 190°C | 190°C | 190°C | 190°C | 3 min | 3 min. | 3 min. | 1.5 min | 1.5 min. | 1.5 min. | 1.5 min. | 1.5 min. |
|
|