Nonisothermal Kinetic Analysis and AC Conductivity for Polyvinyl Chloride (PVC)/Zinc Oxide (ZnO) Nanocomposite

Table 2

The extracted data of the FWO model for both reaction regions of pure PVC.

Alpha PVC	Intercept value	Preexponential (min^-1)	Slope value	Activation energy (kJ/mol)	Statistics Adj.	Average
PVC region 1
0.05	31.08	4.7210^14	-14.95	118.15	1.00	128.11
0.1	31.70	9.1310^14	-15.56	122.97	1.00
0.15	32.31	1.7210^15	-16.04	126.76	1.00
0.2	32.76	2.7710^15	-16.40	129.61	0.99
0.25	32.50	2.1310^15	-16.37	129.37	0.99
0.3	32.53	2.2110^15	-16.48	130.24	1.00
0.35	33.00	3.7310^15	-16.40	126.60	0.98
0.4	32.07	1.3910^15	-16.41	129.69	1.00
0.45	31.67	9.2710^14	-16.29	128.74	1.00
PVC region 2
0.6	33.27	4.9610^15	-17.60	139.09	1.00	145.16
0.65	34.14	1.2310^16	-18.29	144.55	0.99
0.7	34.29	1.4410^16	-18.57	146.76	0.99
0.75	33.72	8.1110^15	-18.42	145.57	0.99
0.8	33.16	4.6210^15	-18.27	144.39	0.98
0.85	33.36	5.7010^15	-18.58	146.84	0.98
0.9	33.44	6.2910^15	-18.84	148.89	0.97