Sealing Performance of New Solidified Materials: Mechanical Properties and Stress Sensitivity Characterization of Pores
Table 2
Test results and parameters of three samples under different confining pressures.
| Sample properties | Sample no. | Confining pressure /MPa | Peak intensity /MPa | Peak strain /mm•mm−1 | Elastic modulus /GPa |
| Concrete material | HN1 | 3.0 | 59.13 | 0.02208 | 3.892 | HN2 | 5.0 | 74.41 | 0.02457 | 4.944 | HN3 | 7.0 | 90.34 | 0.02861 | 5.233 |
| Solidified sealing material | GH1 | 3.0 | 31.09 | 0.02239 | 2.211 | GH2 | 5.0 | 45.61 | 0.02781 | 3.852 | GH3 | 7.0 | 54.78 | 0.03028 | 4.248 |
| Coal sample | MY1 | 3.0 | 15.72 | 0.03096 | 0.545 | MY2 | 5.0 | 25.66 | 0.03541 | 1.330 | MY3 | 7.0 | 31.84 | 0.04157 | 2.083 |
|
|