Electrodeposition of Hydroxyapatite-Multiwalled Carbon Nanotube Nanocomposite on Ti6Al4V
Table 2
The variation of mass, thickness, and adhesion of HAp-MWCNT coatings with the Ti6Al4V substrate.
| MWCNT amount (g/L) | Mass (mg/cm2) | Thickness (μm) ISO 4288-1998 | Adhesion (MPa) |
| 0 | 2.81 ± 0.02 | 8.9 ± 0.82 | 4.5 ± 0.8 | 0.25 | 2.19 ± 0.04 | 6.8 ± 0.61 | 9.2 ± 0.52 | 0.5 | 2.08 ± 0.02 | 6.3 ± 0.84 | 10.4 ± 0.45 | 0.75 | 1.56 ± 0.05 | 4.7 ± 1.05 | 7.1 ± 0.64 | 1 | 1.34 ± 0.08 | 4.1 ± 1.04 | 6.2 ± 0.82 |
|
|