Effects of the Interfacial Bonding Behavior on the Mechanical Properties of E-Glass Fiber/Nanographite Reinforced Hybrid Composites

<table class="table-group" id="tab2"><tr><td><table class="table"><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr class="thead"><td class="align_left">Nanoparticle content in epoxy glass fiber reinforced composite (wt.%)</td><td class="align_center">Flexural strength (MPa)</td></tr><tr><td class="thead-hr" colspan="2"><hr/></td></tr><tr><td class="align_left">0</td><td class="align_center">15.37</td></tr><tr><td class="align_left">1.0</td><td class="align_center">21.87</td></tr><tr><td class="align_left">1.5</td><td class="align_center">22.79</td></tr><tr><td class="align_left">2.0</td><td class="align_center">19.63</td></tr><tr class="table-tr"><td colspan="2"><hr class="tbody-hr"/></td></tr></table></td></tr></table>

<div>Flexural property of nanocomposites.</div>

Advances in Polymer Technology

tab2

Table 2

Table 2: Effects of the Interfacial Bonding Behavior on the Mechanical Properties of E-Glass Fiber/Nanographite Reinforced Hybrid Composites 