Comparison of Conventional Methods and Laser-Assisted Rapid Prototyping for Manufacturing Fixed Dental Prostheses: An In Vitro Study
Table 1
Composition and properties of materials used and their manufacturing processes.
| Product | Process | Alloy composition (Wt %) | Elastic modulus (GPa) | Vickers hardness (Kg/mm²) | Yield strength (MPa, 0.2%) | Thermal expansion coefficient 10−6 µm/mK (25–500°C) |
| Cercon base (DeguDent) Ni-Cr alloy | Lost wax casting | Co 0.1 Cr 14–16 Al 1–3 Ni 71–75 Mo 8–10 Be 0.1–1.9 Traces of Ti | 218 | 360 | 586 | 13.9 |
| StarLoy LS (DeguDent) Co-Cr alloy | Selective laser melting (SLM) | Co 55.2 Cr 18.4 W 18.4 Fe 6.0 Al 2.0 | 210 | 390 | 938–1024 | 14.3 |
| Biologic NA (Conero Dental) Y-TZP | Milling | ZrO2 Y2O3 5% HfO2 <2% Al2O3 and SiO2 <1% | 210 | 1200 | 900–1200 | 10.5 |
|
|