Adhesive | Steps | Composition | Phosphoric acid gel | Application mode | Producer |
|
OptiBond FL (FL) | 3 | Glass, oxide, chemicals, 2-hydroxyethyl methacrylate, ytterbium trifluoride, 3-trimethoxysilylpropyl methacrylate, 2-hydroxy-1,3-propanediyl bismethacrylate, alkali fluorosilicates (Na) | Gel etchant (37.5% phosphoric acid gel) | OptiBond FL Prime was applied with light brushing motion for 15 seconds and then air dried for 5 seconds; using the same applicator; OptiBond FL Adhesive was applied with light brushing motion for 15 seconds and air thinned for 3 seconds | Kerr Corporation, Orange, CA, USA |
|
OptiBond Solo Plus (SO) | 2 | Ethyl alcohol, alkyl dimethacrylate resins, barium aluminoborosilicate glass, fumed silica (silicon dioxide), sodium hexafluorosilicate | Gel etchant (37.5% phosphoric acid gel) | OptiBond Solo Plus was applied with applicator tip for 15 seconds, using light brushing motion, and air thinned for 3 seconds | Kerr Corporation, Orange, CA, USA |
|
Prime & Bond NT (PB) | 2 | Di- and trimethacrylate resins, PENTA (dipentaerythritol penta-acrylate monophosphate), nanofillers-amorphous silicon dioxide, photoinitiators, stabilizers, cetylamine hydrofluoride acetone | Caulk 34% tooth conditioner gel (34% phosphoric acid gel) | Using applicator tip, generous amounts of Prime & Bond NT adhesive to thoroughly wet all the tooth surfaces. The surfaces remained fully wet for 20 seconds; otherwise additional applications of adhesive were applied. Solvent was after that evaporated by methodically blowing with air syringe for at least 5 seconds in order to form adhesive surface with uniform glossy appearance | Dentsply Caulk, Milford, DE, USA |
|
Riva Bond LC (RB) | 2 | Compartment 1: acrylic acid homopolymer, tartaric acid, 2-hydroxyethyl methacrylate, dimethacrylate cross-linker, acidic monomer Compartment 2: glass powder | Super etch 37% phosphoric acid etchant | Capsule was tapped twice on the bench and immediately mixed in an amalgamator for 10 seconds. Using a disposable applicator, Riva Bond LC was applied thinly over the surface of the cavity | SDI Limited, Bayswater, Australia |
|