BioMed Research International / 2017 / Article / Tab 1

Research Article

The Biomineralization of a Bioactive Glass-Incorporated Light-Curable Pulp Capping Material Using Human Dental Pulp Stem Cells

Table 1

The pulp-capping materials tested in this study.

ProductCodeManufacturerLot numberSystemComposition (wt%)

DycalDCDentsply, USA150804Self-curing (calcium hydroxide based)Base paste: 1,3-butylene glycol disalicylate (<50%), calcium tungstate (<20%), zinc oxide (<15%), and so on
Catalyst paste: calcium hydroxide (<55%), zinc oxide (<15%), titanium oxide (<10%), and so on
Theracal LCTCBisco, USA1500006479Light curing (Portland cement based)Portland cement type III (<60%), polyethylene glycol dimethacrylate (<50%), barium zirconate (<10%), and so on
Activa Bioactive™BAPulpdent, USA150814 Light curing (resin based)Blend of diurethane and other methacrylates with modified polyacrylic acid (~53.2%), silica (~3.0%), sodium fluoride (~0.9%), and so on

Composition was filled with the manufacturers’ available information including material safety data sheets.

We are committed to sharing findings related to COVID-19 as quickly as possible. We will be providing unlimited waivers of publication charges for accepted research articles as well as case reports and case series related to COVID-19. Review articles are excluded from this waiver policy. Sign up here as a reviewer to help fast-track new submissions.