Rapid Analyses of Polyetheretherketone Wear Characteristics by Accelerated Wear Testing with Microfabricated Surfaces for Artificial Joint Systems
Table 1
Morphology and wear of PEEK particles in water, FBS, and glycerine.
| Lubricant | Surface | Contact pressure (MPa) | Particle length (μm) | Particle width (μm) | Aspect ratio | Wear rate (mg/min) |
| Water | S | 3.0 | 1.85 ± 0.80 | 1.22 ± 0.54 | 1.56 ± 0.36 | 0.336 | 1.5 | 1.40 ± 0.64 | 0.92 ± 0.41 | 1.56 ± 0.39 | 0.023 | 0.6 | 1.24 ± 0.54 | 0.85 ± 0.36 | 1.51 ± 0.38 | 0.009 | L | 3.0 | 2.80 ± 1.53 | 1.65 ± 0.81 | 1.74 ± 0.54 | 0.382 | 1.5 | 3.13 ± 1.75 | 1.72 ± 1.03 | 1.95 ± 0.73 | 0.185 | 0.6 | 2.29 ± 1.31 | 1.06 ± 0.52 | 2.27 ± 1.07 | 0.056 |
| FBS | S | 3.0 | 1.29 ± 0.60 | 0.77 ± 0.33 | 1.71 ± 0.46 | 0.121 | 1.5 | 0.99 ± 0.41 | 0.57 ± 0.23 | 1.77 ± 0.48 | 0.08 | 0.6 | 0.81 ± 0.34 | 0.48 ± 0.22 | 1.85 ± 0.60 | 0.008 | L | 3.0 | 9.06 ± 3.05 | 5.16 ± 2.05 | 1.89 ± 0.74 | 0.325 | 1.5 | 6.28 ± 2.68 | 3.75 ± 1.57 | 1.75 ± 0.57 | 0.108 | 0.6 | 3.77 ± 1.84 | 1.98 ± 1.32 | 1.91 ± 0.91 | 0.022 |
| 100% Glycerine | S | 1.5 | 0.50 ± 0.31 | 0.28 ± 0.18 | 1.83 ± 0.63 | 0.002 | 50% Glycerine | 0.82 ± 0.41 | 0.53 ± 0.25 | 1.60 ± 0.44 | 0.017 | 10% Glycerine | 1.08 ± 0.59 | 0.73 ± 0.40 | 1.53 ± 0.36 | 0.051 | 100% Glycerine | L | 0.65 ± 0.54 | 0.39 ± 0.28 | 1.73 ± 0.57 | 0.056 | 50% Glycerine | 1.58 ± 1.22 | 0.91 ± 0.60 | 1.76 ± 0.56 | 0.193 | 10% Glycerine | 2.16 ± 1.26 | 1.13 ± 0.62 | 2.02 ± 1.02 | 0.316 |
|
|