Evaluation of the Effect of Different Types of Abrasive Surface Treatment before and after Zirconia Sintering on Its Structural Composition and Bond Strength with Resin Cement Table 1 Materials used in this study.
Material Composition Lot/Manufacturer Zirconia/Ceramill Zi Yttria stabilized polycrystalline tetragonal zirconia (Y-TZP) blank (ZrO2 + HfO2 + Y2O3 99.0) 1512006-1/Amann Girrbach/Koblach/Austria Primer/Scotchbond Universal MDP/Vitrebond copolymer/HEMA/silane/ dimethacrylate resins/fillers/initiators/ethanol 635860/3M ESPE, Germany Resin cement/RelyX Ultimate Base: Methacrylate monomers/radiopaque, silanatedfillers/initiators/stabilizers/ Rheological additives Catalyst: Methacrylate monomers/ radiopaque, alkaline fillers/initiators/stabilizers/pigments/ Rheological additives/fluorescence dye/dark cure activator for Scotchbond Universal adhesive 636403/3M ESPE, Germany Composite resin Filtek Z250, shade A1. (Bis-GMA, UDMA, Bis-EMA, ZrO2/SiO2) 762333/3M ESPE, USA