Evaluation of Dual-Cure Resin Cement Polymerization under Different Types and Thicknesses of Monolithic Zirconia

Table 6

Independent samples t-test and one-way ANOVA results for all measurements. Means followed by different capital letters in the same line and different small letters in the same column were statistically different at p<0.05.

Zirconia thickness	Zirconia type		Measurement depth
		100 µm	300 µm	500 µm
	Mean±SD	Mean±SD		Mean±SD
0.5 mm	PRZ	69.95±5.35 c,A	62.67±4.70 c,B	53.15±7.64 c,C
	PRA	74.69±5.09 b,A	66.06±3.25 b,B	59.03±3.15 b,C
1 mm	PRZ	65.26±2.55 d,A	58.00±4.14 d,B	49.00±3.89 d,C
	PRA	71.22±3.28 c,A	64.58±3.04 c,B	57.51±3.72 b,C
1.5 mm	PRZ	62.80±2.83 e,A	54.15±2.73 e,B	43.64±2.52 e,C
	PRA	65.22±2.96 d,A	58.16±3.68 d,B	50.42±2.25 d,C
2 mm	PRZ	52.10±3.47 f,A	49.33±4.82 f,A	39.41±3.37 e,B
	PRA	54.69±2.79 f,A	51.64±2.60 f,A	42.55±4.69 e,B
Control		124.22±5.42 a,A	119.20±5.77 a,A	100.43±3.75 a,B