Evaluation of Corrosion Behavior by Measuring Passivation Current Density of Dental Implant Coated with Bioceramic Materials
Table 3
Multiple comparison by (LSD) among all pairs for passivation current density parameter in the two materials according to different treated groups.
| | (I) groups | (J) groups | Sig.() | C.S. |
| | Uncoated-1 | Coating with HA-1 | 0.000 | HS | | Coating with zirconia-1 | 0.000 | HS | | Mixture of zirconia and HA-1 | 0.000 | HS | | Uncoated-2 | 0.963 | NS | | Coating with HA-2 | 0.000 | HS | | Coating with zirconia-2 | 0.000 | HS | | Mixture of zirconia and HA-2 | 0.000 | HS | | Coating with HA-1 | Coating with zirconia-1 | 0.508 | NS | | Mixture of zirconia and HA-1 | 0.703 | NS | | Uncoated-2 | 0.000 | HS | | Coating with HA-2 | 0.920 | NS | | Coating with zirconia-2 | 0.860 | NS | | Mixture of zirconia and HA-2 | 0.879 | NS | | Coating with zirconia-1 | Mixture of zirconia and HA-1 | 0.778 | NS | | Uncoated-2 | 0.000 | HS | | Coating with HA-2 | 0.446 | NS | | Coating with zirconia-2 | 0.402 | NS | | Mixture of zirconia and HA-2 | 0.610 | NS | | Mixture of zirconia and HA-1 | Uncoated-2 | 0.000 | HS | | Coating with HA-2 | 0.630 | NS | | Coating with zirconia-2 | 0.577 | NS | | Mixture of zirconia and HA-2 | 0.819 | NS | | Uncoated-2 | Coating with HA-2 | 0.000 | HS | | Coating with zirconia-2 | 0.000 | HS | | Mixture of zirconia and HA-2 | 0.000 | HS | | Coating with HA-2 | Coating with zirconia-2 | 0.000 | NS | | Mixture of zirconia and HA-2 | 0.939 | NS | | Coating with zirconia-2 | Mixture of zirconia and HA-2 | 0.801 | NS |
|
|
()HS: highly significant at ; NS: nonsignificant at . |