Study of Numerical Simulation during ECAP Processing of Can Based on Smooth Particle Hydrodynamics
Table 2
Parameters for constitutive equation of canned materials.
| Material | ρ (kg·m-3) | ν | A (MPa) | B (MPa) | C | m | n |
| industrial pure iron | 7830 | 0.33 | 440 | 510 | 0.014 | 1.03 | 0.26 |
| Tr (K) | Tm (K) | Cv | D1 | D2 | D3 | D4 | D5 |
| 293 | 1793 | 477 | -2.20 | 5.43 | -0.47 | 0.016 | 0.0 |
| Material | ρ (kg·m-3) | ν | A (MPa) | B (MPa) | C | m | n |
| 2024 aluminum alloy | 2770 | 0.3 | 345 | 462 | 0.001 | 2.75 | 0.25 |
| Tr (K) | Tm (K) | Cv | D1 | D2 | D3 | D4 | D5 |
| 293 | 775 | 887 | 0.012 | 0.13 | 1.5 | -0.0175 | 0.0 |
|
|