Exploration of New Electroacupuncture Needle Material
Table 8
Results of safety and economic evaluation according to the material (x: corrosion was not observed. o: corrosion was observed).
| Material | Thickness | Corrosion | Viability (MTT assay) | Viability (stain test) | Cost effectiveness |
| Ti-6Al-4V | 0.20 mm | x | 90.20% | High | Low | PB | 0.25 mm | o | 50.58% | Low | High | Ni co | 0.20 mm | o | 77.83% | Low | Normal | Ni co | 0.25 mm | o | 85.04% | Low | Normal | Ni co | 0.30 mm | o | 81.39% | Low | Normal | SS 316 | 0.20 mm | x | 95.99% | High | Normal | SS 316 | 0.25 mm | x | 96.52% | High | Normal | SS 316 | 0.30 mm | x | 95.90% | High | Normal |
|
|