Wear Characteristics of the Material Specimen and Method of Predicting Wear in Floating Spline Couplings of Aero-Engine
Table 3
Materials and testing conditions.
| Testing couple | Pin (3) | Plate (1) | Load/N | Speed/r·min−1 | Material | Treatment | Material | Treatment |
| 1 | 18CrNi4A | Carburization | 18CrNi4A | Nontreatment | 100 | 200 | 2 | 18CrNi4A | Nontreatment | 18CrNi4A | Nontreatment | 100 | 200 | 3 | 18CrNi4A | Carburization | 32Cr3MoVA | Nontreatment | 100 | 200 | 4 | 18CrNi4A | Nontreatment | 32Cr3MoVA | Nontreatment | 100 | 200 | 5 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 100 | 200 | 6 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 100 | 200 | 7 | 18CrNi4A | Carburization | 32Cr3MoVA | Nitridation | 100 | 200 | 8 | 18CrNi4A | Carburization | 32Cr3MoVA | Nitridation | 100 | 200 | 9 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 50 | 200 | 10 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 120 | 200 | 11 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 150 | 200 | 12 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 100 | 150 | 13 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 100 | 260 | 14 | 18CrNi4A | Carburization | 18CrNi4A | Carburization | 100 | 360 |
|
|
Note: the superscript “” denotes that the material is silvered on the carburization or nitridation layers.
|