Characterization of Thermally Sprayed Coated GT Components Made of 3D Printing Based Selective Laser Melting Processed Inconel Alloy 718

Table 6

Results of substrate temperature on the coatings (at SOD of 120 mm) for both samples.

Substrate temperature in °C	Microhardness in SLM sample	Microhardness in IN718 sample	% porosity in SLM sample	% porosity in IN718 sample	in SLM sample (μm)	in IN718 samples (μm)
35	1100	1000	9.9	6.8	10.2	7.9
100	1130	1025	9.5	6.5	10	7.8
200	1165	1070	8.9	6	9.8	7.5
300	1220	1100	8.2	5.8	9.7	7.4
400	1280	1140	7.4	5.5	9.5	7.3
500	1340	1180	6.9	4.9	9.4	7.1
600	1400	1280	6.1	4.2	9.2	6.8